Products -> High-end Negative Electrode Materials -> MAG-507 high-capacity high-pressure float
  • 产品名称: MAG-507 high-capacity high-pressure float

Physical indicators

Project Work unit Specifications Typical value Test method
Particle size D10 µm ≥8 10.39 Laser scattering method
D50 µm 16-22 19.21 Laser scattering method
D90 µm ≤35 26.63 Laser scattering method
Specific surface area m²/g ≤3.0 1.67 BET method
Apparent density g/cm³ ≥0.60 0.72 Measuring cups
Tap density g/cm³ ≥1.0 1.12 Tap density meter
True density g/cm³ ≥2.20 2.23 He gas replacement
Water % ≤0.10 0.05 GB
Ash % ≤0.15 0.04 GB
Fixed carbon % ≥99.95 99.97 GB
G capacity mAh/g ≥365 367 Analog battery
Coulombic efficiency % ≥94 94.6 Analog battery

 

Characteristic curve
Electron microscope

Material distribution

  Kerby capacity


Product features
 
High discharge capacity, to meet the capacity requirements of high-end products;
High initial charge/discharge efficiency, maximize positive gram capacity;
Excellent processing properties; compacted density;
Superior cycling performance.
Range of application
Suitable for high capacity batteries, can be applied to polymers, aluminum high capacity battery. Meet the digital products, 3G products, standby power supply, portable electronic products, such as the demand of high capacity batteries.

Product application plan
1. materials, proportion and design parameters:
Ratio: MAG-507: conductor: CMC:SBR=95.4%:1.0%:1.6%:2.0% (mass percent), solid 40~45%;
Cathode design capacity on 350mAh/g, excessive 5%.
Compaction density of negative 1.60~1.65g/cm ³,


2. Pulp production:
2.1 required to measure water with CMC, CMC glue added slowly to the water, until no particles in liquid, gel until transparent, stirrer speed revolution speed for 25Hz/min for 30Hz/min, 3h and then rest for 12-24 hours; in the mixing process required circulating water cooling at a temperature not exceeding 35 ℃.
2.2 required number of conductive agents joined the mixer CMC solution and vacuum to do before -0.08mpa, mixing 2H, stirrer speed revolution speed for 30Hz/min for 35Hz/min;
2.3 include the required number of graphite in the mixer mixing 3H and vacuum below -0.08mpa, stirrer speed revolution speed for 30Hz/min for 35Hz/min;
2.4 include the required number of SBR in the mixer mixing 1H, stirrer speed revolution speed for 15Hz/min for 20Hz/min;
2.5 include the required number of H2O in the mixer mixing 2H and vacuum below -0.08mpa, stirrer speed revolution is 15Hz/min, since the speed is 20Hz;
2.6 vent to atmospheric pressure, after passing the test size, 120-150 mesh. Slurry viscosity 1800~2500CP, liquid slurry, paste derived from delicate surfaces, gloss; size in use during vacuum slow stirring, not on hold for a long time.


3. Film production:
3.1 according to the design parameters of the coating.
3.2 pole roller: compaction density of 1.60~1.65g/cm ³, proper adjustment of the roller, roller smooth sheet satisfy processing requirements.


Above parameters for reference, according to the company's technology and equipment to make proper adjustments.

Contact Us
ADD:2nd floor Huabo Building No. 28 Langshan Road, North Area of High-Tech Park, Nanshan District, Shenzhen.
TEL:0755-86240410、27781042
FAX:0755-27579526、26665740
E-mail: baohaiyou@szsinuo.com
URL: http://www.szsinuo.com
Copyright © 2015 Shenzhen Sinuo Industrial Development Co., Ltd. All rights reserved. 粤ICP备09039805号 Powered by www.300.cn