Products -> Power Negative Electrode Materials -> MAG-BCM Super Zoom type
  • 产品名称: MAG-BCM Super Zoom type

Physical indicators

Project Work unit Specifications Typical value Test method
Particle size D10 µm ≥6.0 7.03 Laser scattering method
D50 µm 10~15 13.01 Laser scattering method
D90 µm ≤30 18.90 Laser scattering method
Dmax µm ≤48 32.63 Laser scattering method
Specific surface area m²/g ≤3.0 1.32 BET method
Apparent density g/cm³ ≥0.60 0.62 Measuring cups
Tap density g/cm³ ≥1.00 1.09 Tap density meter
True density g/cm³ ≥2.22 2.23 He gas replacement
Water % ≤0.10 0.08 Gravimetric method
Ash % ≤0.18 0.06 Gravimetric method
Fixed carbon % ≥99.90 99.91 GB
G capacity mAh/g ≥345 350 Analog battery
Coulombic efficiency % ≥91 92.0 Analog battery


Characteristic curve
Electron microscope

Material distribution

   Kerby capacity

Product features
High discharge capacity, high charge/discharge efficiency for the first time;
Good processing properties, the product has strong absorption;
Superior performance and cycle life of tens of thousands of times to meet customer requirements;
Superior low-temperature performance and superior safety performance;
Excellent large current discharge performance, to meet customer 50C rate discharge requirements.
Range of application
Suitable for high-rate, high capacity battery, can be used in electric vehicles, storage batteries, RC airplane, electric tools, electric bicycle, etc.

Product application plan
1. materials, proportion and design parameters:
Ratio: MAG-BCM: conductor: CMC:SBR=95.4%:1.0%:1.6%:2.0% (mass percent), solid content for 40~45%;
Cathode design capacity on 330mAh/g, excess is at least 5%.
Compaction density of negative 1.50~1.55g/cm ³,

2. Pulp production:
2.1 required to measure water with CMC, CMC glue added slowly to the water, until no particles in liquid, gel until transparent, stirrer speed revolution speed for 25Hz/min for 30Hz/min, 3h and then rest for 12-24 hours; in the mixing process required circulating water cooling at a temperature not exceeding 35 ℃.
2.2 required number of conductive agents joined the mixer CMC solution and vacuum to do before -0.08mpa, mixing 2H, stirrer speed revolution speed for 30Hz/min for 35Hz/min;
2.3 include the required number of graphite in the mixer mixing 3H and vacuum below -0.08mpa, stirrer speed revolution speed for 30Hz/min for 35Hz/min;
2.4 include the required number of SBR in the mixer mixing 1H, stirrer speed revolution speed for 15Hz/min for 20Hz/min;
2.5 include the required number of H2O in the mixer mixing 2H and vacuum below -0.08mpa, stirrer speed revolution is 15Hz/min, since the speed is 20Hz;
2.6 vent to atmospheric pressure, after passing the test size, 120 mesh. Slurry viscosity 1800~2500CP, liquid slurry, paste derived from delicate surfaces, gloss; size in use during vacuum slow stirring, not on hold for a long time.

3. Film production:
3.1 according to the design parameters of the coating.
3.2 pole roller: compaction density of 1.50~1.55g/cm ³, proper adjustment of the roller, roller smooth sheet satisfy processing requirements.
Note: our plant for Guangzhou Guan Yu model S-G vacuum mixer

Process for using reference above, according to the company's technology and equipment to make proper adjustments.

Contact Us
ADD:2nd floor Huabo Building No. 28 Langshan Road, North Area of High-Tech Park, Nanshan District, Shenzhen.
E-mail: baohaiyou@szsinuo.com
URL: http://www.szsinuo.com
Copyright © 2015 Shenzhen Sinuo Industrial Development Co., Ltd. All rights reserved. 粤ICP备09039805号 Powered by www.300.cn